Fiberglass Mesh
◆Exterior item
| Specification | Weave | Coating | Tensile Strength | Alkaline Resistance |
| 4*5mm 130g/m2 |
Leno |
Water based Acrylic glue, Alkali resistant |
Warp: ≥1300N/50mmWeft: ≥1500N/50mm |
After 28-Day immersion in 5% Na(OH) solution, the average retention rate for tensile fracture strength ≥70% |
| 5*5mm 145g/m2 | Warp: ≥1300N/50mmWeft: ≥1600N/50mm | |||
| Comply with ETAGstandard 40N/mm
( 1000N/50mm ) |
>50% after testing under the corrosive conditions of standard BS EN 13496 | |||
| 4*4mm 160g/m2 | LenoWarp Knitting | |||
|
4*4mm 152g/m2 |
Leno for 38” Warp Knitting for 48” |
Water based
Acrylic glue, Flame retardant |
The Warp KnittingStucco mesh
meet the minimum requirements Condition of Acceptance in ASTM E2568 |
After 28-Day immersion in 5% Na(OH) solution, the average retention rate for tensile fracture strength ≥70% |
◆Application
Specification & sizes can be customized according to the practical application of the product.
Mainly used with exterior wall putty to reinforce the surface and prevent cracking. External thermal insulation system, EIFS system, ETICS system,GRC.
◆Interior item
| Specification | Weave | Coating | Tensile Strength | Alkaline Resistance |
| 9*9yarn/inch 70g/m2 | Warp Knitting |
Water based Acrylic glue, Alkali resistant |
Warp: ≥600N/50mm
Weft: ≥500N/50mm |
After 28-Day immersion in 5% Na(OH) solution, the average retention rate for tensile fracture strength ≥70% |
| 5*5mm 75g/m2 |
Leno |
Warp: ≥600N/50mm
Weft: ≥600N/50mm |
||
| 4*5mm 90g/m2 | Warp: ≥840N/50mm
Weft: ≥1000N/50mm |
|||
| 5*5mm 110g/m2 | Warp: ≥840N/50mm
Weft: ≥1100N/50mm |
|||
| 5*5mm 125g/m2 | Warp: ≥1200N/50mm
Weft: ≥1350N/50mm |
◆Application
Specification & sizes can be customized according to the practical application of the product.
Mainly used with exterior wall putty to reinforce the surface and prevent cracking. Cement and gypsum wall.
◆Package
Each roll with or in plastic bag or shrink wrap with label or without label
2 inch paper core
With carton box or pallet
◆Complex item
| Specification | Size | Weave | Coating | Application Performance | Alkaline
Resistance |
| 9*9yarn/inch 70g/m2 | 1*50m | Warp Knitting |
Water based Acrylic glue, SBR, Asphalt, etc. Alkali resistant |
Soft, Flat |
After 28-Day immersion in 5% Na(OH) solution, the average retention rate for tensile fracture strength ≥70% |
| 20*10yarn/inch 60g/m2 |
Width:100~200cm Length:200/300m |
Plain | |||
| 3*3mm 60g/m2 |
Leno |
||||
| 2*4mm 56g/m2 | Flexible, Soft, Flat, Easy to unroll | ||||
| 5*5mm 75g/m2 | 1m/1.2m*200m;
16cm*500m |
Soft, Flat |
|||
| 5*5mm 110g/m2 | 20cm/25cm*600m;
28.5cm/30cm*300m; 0.9m/1.2m*500m; |
||||
| 5*5mm 145g/m2 | 20cm/25cm*500m; 0.65m/1.22m*300m; |
◆Application
Specification & sizes can be customized according to the practical application of the product.
Mainly used to reinforce of Marble, Mosaic, PVC Profile, Rock wool board, XPS board, Cement board, Geogrid, non-woven.
◆Adhesive item
Product: Self-adhesive Fiberglass Mesh
| Specification | Size | Weave | Coating | Application
Performance |
Alkaline
Resistance |
| 4*5mm 90g/m2 | 1m*50m;
17/19/21/22/25/35mm*150m; |
Leno |
Water based Acrylic glue, SBR, Asphalt, etc. Alkali resistant, Self adhesive; |
Self-adhesion; Initial adhesion ≥120S (180°position, 70g hung), Enduring adhesion ≥30Min (90°position, 1kg hung); Easy to unroll; |
After 28-Day immersion in 5% Na(OH) solution, the average retention rate for tensile fracture strength ≥60% |
| 5*10mm 100g/m2 | 0.89m*200m; | ||||
| 5*5mm 125g/m2 | 7.5cm/10cm/15cm/1m/1.2m*50m; 21/35mm*150m; | ||||
| 5*5mm 145g/m2 | 10cm/15cm/1m/1.2m*50m;
20cm/25cm*500m; 0.65m/1.22m*300m; |
||||
| 5*5mm 160g/m2 | 50/150/200/1195mm*50m; | ||||
| 10*10mm 150g/m2 | 60cm*150m; |
◆Application
Specification & sizes can be customized according to the practical application of the product.
Mainly used to reinforce of complicated model, EPS model, Foam model, Floor heating system.
◆Quality Contro
We use special glue techniques, apply advanced manufacturing technology and reliable materials.
A. The meshis strong, durable and fixed very firm (not easy to move).
B. The meshis regular, clear and smooth without pricking hands, because we produce the fiberglass yarn by ourselves.
C. The flame retardant EIFS mesh is soft and have good characteristics of flame retardant because we use high quality flame retardant coating.